| Título: | Avaliação do desempenho de painéis de madeira lamelada colada cruzada utilizando diferentes tecnologias |
| Outros títulos: | Performance evaluation of crosslaminated timber panels using different technologies |
| Autor(es): | Carvalho, Joyce Granjeiro de |
| Orientador(es): | Pace, José Henrique Camargo |
| Assunto: | Painéis de madeira
Construção civil
Madeira |
| Data de apresentação: | 31-Jan-2025 |
| Data de publicação: | 23-Dez-2025 |
| Referência: | CARVALHO, Joyce Granjeiro de. Avaliação do desempenho de painéis de madeira lamelada colada cruzada utilizando diferentes tecnologias. 2025. 47 f., il. Trabalho de Conclusão de Curso (Bacharelado em Engenharia Florestal) — Universidade de Brasília, Brasília, 2025. |
| Resumo: | Os painéis de Madeira Laminada Colada Cruzada (CLT) confeccionados com Allantoma
decandra, madeira oriunda de concessão florestal, usando peças inteiriças e emendas dentadas,
foram avaliados por ensaios de ultrassom, ondas de tensão e flexão estática. Os módulos de
elasticidade (MOE) não apresentaram diferenças significativas entre os tipos de painéis,
enquanto os módulos de ruptura (MOR) mostraram diferenças estatisticamente significativas.
Os valores de MOE e MOR foram considerados excelentes, atendendo às exigências da norma
ANSI/APA PRG 320-2018. Entre os métodos avaliados, o stress wave foi o que mais se
aproximou dos resultados obtidos pela flexão estática, embora a correlação entre os métodos
destrutivos e não destrutivos tenha sido baixa. As emendas dentadas não impactaram
significativamente o MOE e tiveram pouca influência no MOR, mas estudos adicionais com
mais amostras são recomendados para validar os ensaios não destrutivos como ferramentas
preditivas. |
| Abstract: | The Cross-Laminated Timber (CLT) panels made with Allantoma decandra, wood sourced
from forest concessions, using solid pieces and finger joints, were evaluated through ultrasonic
tests, stress wave tests, and static bending tests. The modulus of elasticity (MOE) showed no
significant differences between the types of panels, while the modulus of rupture (MOR)
exhibited statistically significant differences. The MOE and MOR values were considered
excellent, meeting the requirements of the ANSI/APA PRG 320-2018 standard. Among the
methods evaluated, the stress wave test most closely matched the results obtained from static
bending, although the correlation between destructive and non-destructive methods was low.
Finger joints did not significantly impact the MOE and had little influence on the MOR, but
further studies with a larger sample size are recommended to validate non-destructive tests as
predictive tools. |
| Informações adicionais: | Trabalho de Conclusão de Curso (graduação) — Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Florestal, 2025. |
| Licença: | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor que autoriza a Biblioteca Digital da Produção Intelectual Discente da Universidade de Brasília (BDM) a disponibilizar o trabalho de conclusão de curso por meio do sítio bdm.unb.br, com as seguintes condições: disponível sob Licença Creative Commons 4.0 International, que permite copiar, distribuir e transmitir o trabalho, desde que seja citado o autor e licenciante. Não permite o uso para fins comerciais nem a adaptação desta. |
| Aparece na Coleção: | Engenharia Florestal
|
Todos os itens na BDM estão protegidos por copyright. Todos os direitos reservados.